Zafari, A.; Xia, K.
Scripta materialia, November 2016, 2016-11-00, 20161101, Letnik: 124Journal Article
Careful TEM examination has confirmed the formation of equiaxed α in nanocrystalline β during ageing of a severely deformed metastable β Ti alloy. It is revealed that the Burgers orientation relationship is obeyed upon α nucleation, but grain growth has led to the eventual incoherent α/β interfaces. In addition, intragranular acicular α would form when the β grains prior to ageing are much coarser than ~10nm. Display omitted
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.