Xue, S.W.; Zu, X.T.; Zhou, W.L.; Deng, H.X.; Xiang, X.; Zhang, L.; Deng, H.
Journal of alloys and compounds, 01/2008, Letnik: 448, Številka: 1Journal Article
ZnO thin film was deposited onto (0 0 0 1) sapphire substrate by a sol–gel method. The as-prepared film was annealed at different temperatures from 600 to 950 °C in argon ambient. Transmittance spectra were used to determine the optical constants of the annealed ZnO film, and the effects of the annealing temperature on the optical constants were investigated. Transmittance measurement shows that the absorption edge blueshifts when the annealing temperature is below 750 °C while redshifts when the annealing temperature exceeds 750 °C. With increasing the annealing temperature, the optical constant of ZnO film decreases in the ultraviolet region while increases in the visible region.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.