Kocaman, Mücahit; Akçay, Serhatcan Berk; Güler, Onur; Çuvalcı, Hamdullah; Varol, Temel; Çuvalcı, Oğuzhan
Tribology international, October 2023, 2023-10-00, Letnik: 188Journal Article
In this study, effect of recycled zinc powder reinforcement ratios and ball milling time on novolac matrix hybrid composites were investigated. The ball milling time of 2 h showed a positive effect on the hardness of the composites up to 100 HRM. Thermal analysis results showed that the increasing zinc reinforcement ratio was increased thermal stability of the composite powders. The assessment of wear resistance was conducted using a block-on-ring tribometer, and the results demonstrated that the incorporation of zinc particles significantly decreased wear rates. Additionally, 2 h ball milling times showed superior wear resistance. Specimens with 20 wt% Zn reinforcement and subjected to 2 h ball milling time exhibited approximately 93% less wear loss than Zn-free specimens. •Zinc powder recycled from waste Zinc anode.•Novolac matrix Zinc reinforced hybrid composites synthesized.•Thermal stability was increased with increasing Zinc reinforcement ratio.•The highest hardness value was obtained as 100 HRM.•The minimum wear rate in this study was obtained as 0.39 × 10−5 mm3/N.m.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.