Tranchida, G.; Clesi, M.; Di Franco, F.; Di Quarto, F.; Santamaria, M.
Electrochimica acta, 05/2018, Letnik: 273Journal Article
Passive films were grown at constant potential in acidic (pH∼2) and alkaline (pH∼13) solutions on chromium, AISI 304L, AISI 316L and Duplex stainless steels. Passive films on chromium grow following a high field mechanism considering the presence of dissolution phenomena. According to the photoelectrochemical characterization, passive films on Cr have a bandgap of 3.4 eV when formed in acidic solution, and of 2.4 eV when formed in alkaline solution due to the formation of Cr(OH)3. These films result to be poorly stable against anodic dissolution due to a very anodic flat band potential. Conversely, impedance and photoelectrochemical measurements proved that passive films on stainless steels are chromium rich oxide n-type semiconductors with a very high polarization resistance. Their band gap depends on the pH of the passivation solution and on the SS composition.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.