Reis, T.M.; Boeira, C.D.; Serafini, F.L.; Farias, M.C.M.; Figueroa, C.A.; Michels, A.F.
Surface & coatings technology, 05/2022, Letnik: 438Journal Article
Copper‑beryllium alloys are widely used to manufacture thermoplastics injection molds due to their high thermal conductivity. Even though these alloys admit precipitation hardening at temperatures between 250 and 400 °C, they still call for surface coatings to enhance their abrasion resistance. However, application of these coatings can generate over-aging under specific deposition temperature ranges. This phenomenon causes a loss of substrate mechanical properties, making some industrial applications unfeasible, for example: construction of core pins with high slenderness ratio, and cores and cavities injection mold with narrow closure regions. This work proposes a solution to increase abrasive wear resistance of copper‑beryllium alloy C17200 through an electroless nickel‑phosphorus (NiP) coating. Temperature used in heat treatment of the coating was lower than substrate aging temperature. In this work, the heat treatment was carried out at 200 °C for 24 h. Hardness of coating and substrate was evaluated by measuring the cross-sectional microhardness profile after heat treatment. Microstructure, chemical composition, and crystallinity of coating and substrate were characterized using scanning electron microscopy (SEM), glow discharge optical emission spectroscopy (GD-OES), and X-ray diffraction (XRD), respectively. Wear behavior of coating-substrate systems was evaluated by micro-abrasive wear tests optical profilometry and SEM. NiP coating combined with heat treatment increased the surface hardness from 340 HV for uncoated alloy to an average of 997 HV for coated and heat treated alloy while maintaining substrate hardness. The application of this coating reduced the wear coefficient in the order of 3.03 × 10−6 to 2.04 × 10−6 (mm3 N−1 m−1). All the conditions analyzed, showed a mixed micro-abrasive wear mechanism with rolling and grooving wear characteristics. Display omitted •Electroless nickel-phosphorus (NiP) coating applied on CuBe alloy C17200.•Coating process temperature lower than copper‑beryllium alloy aging temperature.•Coating NiP combined with heat treatment reduce the wear coefficient.•Increased wear resistance of CuBe alloy without changing substrate properties.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.