Olszewski, J.; Zbroszczyk, J.; Hasiak, M.; Kaleta, J.; Nabiałek, M.; Brągiel, P.; Sobczyk, K.; Ciurzyńska, W.; Świerczek, J.; Łukiewska, A.
Journal of rare earths, 08/2009, Letnik: 27, Številka: 4Journal Article
The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67CosNd3Y6B19 alloy, inhomogeneous in the as-quenched state, crystallized after annealing at 948 K for 0.5 h and consisted of Nd2Fe14B-type, Fe2B and paramagnetic phases. The rapidly solidified Fe64Co5Nd6Y6B19 alloy contained the Nd2Fel4B-type and paramagnetic phases. The annealing of the bulk Fe67CosNd3Y6B19 alloy at 948 K for 0.5 h led to hard magnetic properties. However, the bulk Fe64Co5Nd6Y6B19 alloy exhibited good hard magnetic properties directly after preparation.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.