McCarthy, B.P.; Pederson, L.R.; Chou, Y.S.; Zhou, X.-D.; Surdoval, W.A.; Wilson, L.C.
Journal of power sources, 05/2008, Letnik: 180, Številka: 1Journal Article
Electrical contact pastes of composition (La 0.90Sr 0.10) 0.98MnO 3 + δ (LSM-10) formed strong bonds (∼3 MPa) to (Co,Mn) 3O 4 spinel-coated Crofer 22 APU ferritic steel coupons when exposed to alternating flows of air and nitrogen (10 ppm O 2) at 900 °C for 2 h or longer. When held at 900 °C in air only, bond strengths were negligible. Substantial bonds could also be created between LSM-10 contact paste and (La 0.80Sr 0.20) 0.98MnO 3 + δ (LSM-20) porous cathodes by processing in alternating air and nitrogen, without simultaneous densification of the cathode. Enhanced sintering of LSM-10 is attributed to transients in the defect structure induced by oxygen partial pressure changes.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.