Kuznetsov, Boris N; Chudina, Anna I; Kazachenko, Aleksandr S; Fetisova, Olga Yu; Borovkova, Valentina S; Vorobyev, Sergei A; Karacharov, Anton A; Gnidan, Elena V; Mazurova, Elena V; Skripnikov, Andrey M; Taran, Oxana P
Polymers, 06/2023, Letnik: 15, Številka: 12Journal Article
A new method for extractive-catalytic fractionation of aspen wood to produce microcrystalline (MCC), microfibrillated (MFC), nanofibrilllated (NFC) celluloses, xylan, and ethanollignin is suggested in order to utilize all of the main components of wood biomass. Xylan is obtained with a yield of 10.2 wt.% via aqueous alkali extraction at room temperature. Ethanollignin was obtained with a yield of 11.2 wt.% via extraction with 60% ethanol from the xylan-free wood at 190 °C. The lignocellulose residue formed after the extraction of xylan and ethanollignin was subjected to catalytic peroxide delignification in the acetic acid-water medium at 100 °C in order to obtain microcrystalline cellulose. MCC is hydrolyzed with 56% sulfuric acid and treated with ultrasound to produce microfibrillated cellulose and nanofibrillated cellulose. The yields of MFC and NFC were 14.4 and 19.0 wt.%, respectively. The average hydrodynamic diameter of NFC particles was 36.6 nm, the crystallinity index was 0.86, and the average zeta-potential was 41.5 mV. The composition and structure of xylan, ethanollignin, cellulose product, MCC, MFC, and NFC obtained from aspen wood were characterized using elemental and chemical analysis, Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) analyses, Gas chromatography (GC), Gel permeation-chromatography (GPC), Scanning electron microscopy (SEM), Atomic force microscopy (AFM), Dynamic light scattering (DLS), Thermal gravimetric analysis (TGA).
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.