PALAN, C B; BAJAJ, N S; SONI, A; KULKARNI, M S; OMANWAR, S K
Bulletin of Materials Science/Bulletin of materials science, 10/2015, Letnik: 38, Številka: 6Journal Article
The polycrystalline sample of LiBaPO 4 : Tb 3+ (LBPT) was successfully synthesized by solution combustion synthesis and studied for its luminescence characteristics. The thermoluminescence (TL) glow curve of LBPT material consists of two peaks at 204.54 and 251.21°C. The optimum concentration was 0.005 mol to obtain the higher TL intensity compared to commercial TLD-100 phosphor. The peak shape method was used to calculate kinetic parameter (activation energy and frequency factor). In CW-OSL mode its sensitivity for beta exposure was found to be 50% compared to commercially available α -Al 2 O 3 : C and 40% than LMP (BARC), and photoluminescence spectrum of LBPT shows green emission when excited with 225 nm UV source.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.