Chen, Bing Qing; Xing, Wei Jie; Jiang, Tao; Wei, Zhen Wei
Materials science forum, 05/2021, Letnik: 1032Journal Article
ZTC4 alloy prepared by electron beam melting was hot isostatically pressed, the macro-and microstructure were characterized by stereo microscopy and optical microscopy, the tensile properties were tested and the fracture profiles were characterized using scanning electron microscopy. The results show that: The vertical deposition samples exhibit coarsen epitaxial columnar grains and the parallel samples show equiaxed grains, and microstructure are basket-weave α+β phase. The vertical deposition samples exhibit very high ultimate tensile strength and yield strength but poor ductility with elongation and shrinkage, and show generally more planar and faceted fracture morphology. The anisotropy in tensile properties is mainly due to the difference in the orientation of the columnar grains with respect to the tensile test direction, and the characteristics of the minor fracture plane are mainly related to the α colonies.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.