Li, Yi Nan; Peng, Zi Long; Zhang, Shan Bin
Applied Mechanics and Materials, 07/2014, Letnik: 595, Številka: Recent Engineering Decisions in IndustryJournal Article
He-GTA welding of 10mm thick copper plates by using independent developed welding material - CuTi alloys was investigated. The crystal crack induced by eutectic of Cu and Cu2O is disappeared completely as the addition of deoxidant element Ti. It can be concluded that the Ti inhibits the formation of Cu2O and combines with O to generate TiO2 through the thermal dynamical calculation. As the TiO2 has the characteristic of high molt point and low density, TiO2 flows upward to surface of molten pool during welding and forms as weld slag at the weld surface after cooling, then the uniform microstructure without crystal crack is obtained finally. In all GTA welding specimens tested, the failure is located in the heat affected zone and the tensile strength is similar to the base metal.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.