Liu, Qing; Ding, Jiang; Mante, Francis K; Wunder, Stephanie L; Baran, George R
Biomaterials, 08/2002, Letnik: 23, Številka: 15Journal Article
Surface functional groups play important roles in nucleating calcium phosphate deposition on surgical titanium implants. In this study, various functional groups were introduced onto the surface of commercially pure titanium foils using a self-assembled monolayer (SAM) technique. An organic silane, 7-oct-1-enyltrichlorosilane (OETS) was used and OH, PO 4H 2, COOH groups were derived from its unsaturated double bond. Ti foils were first oxidized in concentrated H 2SO 4/H 2O 2. ESCA and contact angle measurements were used to characterize the SAM surfaces and confirm the presence of various functional groups. A fast calcium phosphate deposition experiment was carried out by mixing Ca 2+- and (PO 4) 3−-containing solutions in the presence of the surface-modified Ti samples at pH 7.4 at room temperature in order to verify the nucleating abilities of these functional groups. SEM, Raman spectroscopy, XRD and ATR-FTIR results showed that poorly crystallized hydroxyapatite (HA) can be deposited on the SAM surfaces with PO 4H 2 and –COOH functional groups, but not onto the SAM with –CHCH 2 and –OH. –PO 4H 2 exhibited a stronger nucleating ability than that of –COOH. The oxidized Ti sample also showed some calcium phosphate deposition but to a lesser extent as compared to SAM surfaces with –PO 4H 2 and –COOH. The pre-deposited HA can rapidly induce biomimetic apatite layer formation after immersion in 1.5 SBF for 18 h regardless of the amount of pre-deposited HA. The results suggested that the pre-deposition of HA onto these functionalized SAM surfaces might be an effective and fast way to prepare biomimetic apatite coatings on surgical implants.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.