Soares, Vagner F. G.; Ramirez, Daniel A.; Damasceno, Igor Z.; Echevirrigaray, Fernando G.; Figueroa, Carlos A.; Perotti, Bruna L.; Serafini, Francisco L.; Oliveira, Givanilson B.; Terto, André R.; Tentardini, Eduardo K.
Materials research (São Carlos, São Paulo, Brazil), 2021, Letnik: 24, Številka: 1Journal Article
Abstract Iso and non-iso architected TiN/Cr multilayers with constant composition were deposited by balanced magnetron sputtering aiming to investigate the influence of different architectures over coatings structures and properties. Glow discharge optical emission spectroscopy analyses were used to determine in-depth constituents and suggested that no diffusion of elements occurred between layers in room temperature. Field emission gun scanning electron microscopy analyses showed that all multilayers presented sharp interfaces and low porosity microstructures, with column-like grain growth influenced by layer sizes. Glancing angle X-ray diffraction analyses showed that multilayers consist of polycrystalline α-Cr and δ-TiN phases with a main peak in Cr(110) plane. The overlapping of TiN onto metallic layers led to the suppression of growth in the TiN(111) plane, although TiN layers thicker than 50 nm demonstrated a growth in plane TiN(200). Nanoindentation tests registered equal hardness values for all multilayers of around 16.2 GPa, on the other hand, a tendency to improve hardness has been identified for hierarchical multilayer. Oxidation tests revealed that architectures with thicker TiN top layers presented an improved oxidation resistance up to 600 ºC, probably due to growth in more compact TiN(200) plane. However, TiN/Cr coatings did not resist integrally to oxidation tests at 750 ºC.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.