Shafiu, S; Uenal, B; Baykal, A
Journal of superconductivity and novel magnetism, 04/2014, Letnik: 27, Številka: 4Journal Article
Polyaniline-MnFe sub(2)O sub(4)-CTAB nanocomposite was successfully synthesized by using 1-butyl-3-methyl-imidazolium trifluoromethane sulfonate (RTILs) as ionic liquid and Cetyl trimethylammonium bromide (CTAB) as surfactant via in-situ polymerization. The calculated average crystallite size, D sub(XRD), of the product was 26 plus or minus 4 nm. Conductivity and permittivity properties of Polyaniline-MnFe sub(2)O sub(4) nanocomposite was also exemplified by means of an impedance spectroscopy, which would be evaluated at frequency ranges up to 3 MHz for temperature range of 20-120 degree C. In general, ac conductivity remains almost unchanged until it reaches up to 160 kHz, and then reduces slightly almost for all temperatures except for some slight fluctuation somehow at lower temperatures. The values fluctuate between 1.1-1.6 mS/cm at above all temperatures.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.