Grigorova, Eli; Spassova, Maya; Spassov, Tony; Khristov, Mitko
Journal of materials science, 03/2014, Letnik: 49, Številka: 6Journal Article
The hydriding/dehydriding characteristics of 90 wt% MgH2a10 wt% MeSi2 (Me = Ti, Cr) composites, synthesized by ball milling under argon, were studied by Sievertas type apparatus and by high-pressure differential scanning calorimetry (HPDSC). The composites have demonstrated similar absorption kinetics and capacity at temperature of 300 degree C and a pressure of 1 MPa. They showed fast kinetics and achieved absorption capacity higher than 6 wt%. Slightly higher values for the enthalpy of hydriding and dehydriding were obtained at scanning conditions in the HPDSC for the composite 90 wt% MgH2a10 wt% CrSi2 compared to those for the composite with addition of TiSi2.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.