Characterization of cast A▫$l_{86}Mn_3Be_{11}▫$ alloy
Bončina, Tonica ; Markoli, Boštjan ; Zupanič, Franc
An Al86Mn3Be11 alloy cast into copper mould was subjected to metallographic investigation. The as-cast microstructure consisted of a quasicrystalline icosahedral phase (i-phase), Be4AlMn phase and, ...occasionally, a hexagonal phase. Al-rich solid solution represented the dominant phase. The chemical compositions of phases were determined using AES. The composition of the Be4AlMn slightly deviated from the stoichiometric composition, whereas the composition of the i-phase was approximately Al52Mn18Be30, containing an appreciable amount of Be. The average composition of the hexagonal phase was Al66Mn21Be13. Deep etching and particle extraction provided a deep insight into the three-dimensional morphology of the i-phase and the hexagonal phase, whereas Be4AlMn was slightly attacked by the etchant. The i-phase was present predominantly in the form of dendrites and a rodlike eutectic phase. The hexagonal phase was primarily in the form of hexagonal platelets, whereas Be4AlMn was rather irregular in shape. The morphology of the i-phase can be explained by predominant growth in 3-fold directions and the lowest energy of the 5-fold planes, leading to the faceting and adopting a pentagonal dodecahedron shape. The brightnesses of phases in the backscattered electron images were rationalized by determining their backscattering coefficients. TEM investigation showed considerable phason strain in the i-phase, and the polycrystalline nature of the Be4AlMn phase.
It was not necessary to add the material to the shelf.
Bibliographic material was successfully added on shelf.
Adding bibliographical material on shelf was not successful.
Material is already on the shelf.
Permalink
URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year
Impact factor
Edition
Category
Classification
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Impact factor
Select the library membership card:
DRS,
in which the journal is indexed
Database name
Field
Year
Links to authors' personal bibliographies
Links to information on researchers in the SICRIS system
Subject headings in COBISS General List of Subject Headings
Select pickup location
The material from the parent unit is free. If the material is delivered to the pickup location from another unit, the library may charge you for this service.