Effects of laser shock processing on high cycle fatigue crack growth rate and fracture toughness of aluminium alloy 6082-T651
Bergant, Zoran ; Trdan, Uroš ; Grum, Janez, 1946-
The effects of laser shock processing without protective coating on high-cycle fatigue crack growth and fracture toughness were investigated. Laser shock peening treatment was performed on compact ...tension specimens from both sides perpendicular to the crack growth direction, followed by subsequent grinding. Fatigue crack growth tests were performed at frequencies between 116 and 146 Hz, at R = 0.1 and a constant stress intensity range during the fatigue crack initiation phase and K-decreasing test. A lower number of cycles was required to initiate a fatigue precrack, and faster fatigue crack growth was found in tensile residual stress field of LSP-treated specimens. The crack growth threshold decreased by 60% after LSP treatment. The fracture toughness decreased by 28-33% after LSP treatment. The fatigue-to-ductile transition boundary on fractographic surfaces show linear fatigue crack fronts in non-treated specimens and curves after LSP treatment.
It was not necessary to add the material to the shelf.
Bibliographic material was successfully added on shelf.
Adding bibliographical material on shelf was not successful.
Material is already on the shelf.
Permalink
URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year
Impact factor
Edition
Category
Classification
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Select the library membership card:
DRS,
in which the journal is indexed
Database name
Field
Year
Links to authors' personal bibliographies
Links to information on researchers in the SICRIS system
Subject headings in COBISS General List of Subject Headings
Select pickup location
The material from the parent unit is free. If the material is delivered to the pickup location from another unit, the library may charge you for this service.
PDF