Electrochromic ▫$Ni_1-xO$▫ pigment coatings and plastic film-based ▫$Ni_1-x0/Ti0_2$▫ device with transmissive light modulation
Mihelčič, Mohor ...
Novel nickel oxide coatings (100-600 nm in thickness) with low surface roughness (<20 nm) and haze levels down to 6% were deposited at a temperature not higher than 150 °C on FTO glass and conducting ...plastic films. The coatings were deposited on the substrates from water dispersions made of Ni1-xO pigment synthesized via the peroxo route by reaction of a H2O2/urea mixture with Ni-acetate precursor. The bunsenite Ni1-xO pigment was obtained after thermal treatment of xerogels at 400 °C for 24 h. Processing common for paint manufacturing was applied for the preparation of water dispersions of the Ni1-xO pigment, i.e., intensive milling of the pigment with dispersant. Dispersant (NiOxHy) was prepared by colloidal precipitation technique from Ni-sulfate precipitated with sodium hypochlorite. The materials (Ni1-xO pigment, NiOxHy precipitate, coatings) were investigated using various analytical techniques (TG, DSC, SEM, TEM, IR and optical spectroscopy), while the electrochromic properties were determined by means of in situ spectroelectrochemical measurements, applying standard electrochemical techniques (cyclic voltammetry, chronocoulometry). The results revealed a convenient, simple, and robust technique for making "electrochromic paint" coatings from pre-prepared Ni1-xO pigment. They demonstrate the potential of the described electrochromic coatings for manufacturing plastic film based electrochromic devices providing transmissive light modulation.
It was not necessary to add the material to the shelf.
Bibliographic material was successfully added on shelf.
Adding bibliographical material on shelf was not successful.
Material is already on the shelf.
Permalink
URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year
Impact factor
Edition
Category
Classification
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Impact factor
Select the library membership card:
DRS,
in which the journal is indexed
Database name
Field
Year
Links to authors' personal bibliographies
Links to information on researchers in the SICRIS system
Subject headings in COBISS General List of Subject Headings
Select pickup location
The material from the parent unit is free. If the material is delivered to the pickup location from another unit, the library may charge you for this service.