Comparative analysis of inactivated wood surfaces : dissertation submitted to the Faculty of Virginia Polytechnic Institute and State University in partial fulfillment of the requirements for the degree of Doctor of Philosophy in Wood Science and Forest Products
Šernek, Milan
A wood surface, which is exposed to a high temperature condition, can experience inactivation. Surface inactivation results in reduced ability of an adhesive to properly wet, flow, penetrate, and ...cure. Thus, an inactivated wood surface does not bond well with adhesives. The changes in surface chemistry, wettability, and adhesion of inactivated wood surfaces, including heartwood of yellow-poplar (Liriodendron tulipifera) and southern pine (Pinus taeda), were studied. Wood samples were dried from the green moisture content condition in a convection oven at five different temperature levels ranging from 50 to 200 °C. The comparative characterization of the surface was done by X-ray photoelectron spectroscopy (XPS), sessile drop wettability, and fracture testing of adhesive bonds. The oxygen to carbon ratio (O/C) decreasedand the C1/C2 ratio increased with drying temperature. The C1 component is related to carbon-carbon or carbon-hydrogen bonds, and the C2 component represents single carbon-oxygen bond. A low O/C ratio and a high C1/C2 ratio reflected a high concentration of non-polar wood components (extractives/VOCs) on the wood surface, which modified the wood surface from hydrophilic to more hydrophobic. Wettability was directly related to the O/C ratio and inversely related to the C1/C2 ratio. Contact angle decreased with time and increased with the temperature of exposure. Southern pine had a lower wettability than yellow-poplar, which was due to a greater concentration of non-polar hydrocarbon-type extractives and heat-generated volatiles on the surface. Solvent extraction prior to drying did not improved wettability, whereas, extraction after drying improved wettability. A contribution of extractives migration and VOCs generation played a significant role in the heat-induced inactivation process of southern pine. The maximum strain energy release rate (Gmax) showed that surface inactivation was insignificant for was most susceptible to inactivation at drying temperatures > 156°C, particularly when bonded with phenol-formaldehyde (PF) adhesive. Chemical treatments improved the wettability of inactivated wood surfaces, but an improvement in adhesion was not evident for specimens bonded with polyvinyl-acetate (PVA) adhesive. NaOH surface treatment was most effective for improving adhesion of the PF adhesive bond. yellow-poplar when exposed to drying temperatures < 187°C. The southern pine
Type of material - dissertation
; adult, serious
Publication and manufacture - Blacksburg Virginia : [M. Šernek], 2002
It was not necessary to add the material to the shelf.
Bibliographic material was successfully added on shelf.
Adding bibliographical material on shelf was not successful.
Material is already on the shelf.
Permalink
URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year
Impact factor
Edition
Category
Classification
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Select the library membership card:
DRS,
in which the journal is indexed
Database name
Field
Year
Links to authors' personal bibliographies
Links to information on researchers in the SICRIS system
Subject headings in COBISS General List of Subject Headings
Select pickup location
The material from the parent unit is free. If the material is delivered to the pickup location from another unit, the library may charge you for this service.