Shi, S.J.; Tu, J.P.; Tang, Y.Y.; Liu, X.Y.; Zhao, X.Y.; Wang, X.L.; Gu, C.D.
Journal of power sources, 11/2013, Volume: 241Journal Article
Cube-like and plate-like LiLi0.2Mn0.54Ni0.13Co0.13O2 particles are obtained after treated in LiCl and KCl molten salts at 800 °C, respectively, comparing to the ball-like original particles calcined in air. The oxide treated in KCl molten salt with large specific area of 17.05 m2 g−1 delivers high discharge capacities of 254.1 mAh g−1 and 168.5 mAh g−1 at current densities of 200 mA g−1 and 2000 mA g−1, respectively. In addition, enhanced cycle stability with capacity retention of 94.9% after 80 cycles at charge–discharge current densities of 200 mA g−1 is obtained for the oxide treated in LiCl molten salt with sacrifice of a little capacity. Such electrochemical performance change is proved to be independent of Li+ diffusion coefficient. It appears that the treatment in molten salts can effectively reform the electrochemical performances of LiLi0.2Mn0.54Ni0.13Co0.13O2 cathode materials for various applications. •Cube and plate-like particles are obtained after treated in LiCl and KCl molten salts.•Oxide treated in KCl molten salt has large specific area of 17.05 m2 g−1.•And discharge capacity of 168.5 mAh g−1 is obtained at 10 C.•Oxide treated in LiCl molten salt has enhanced capacity retention of 94.9%.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.