Development of an Al-Mn-Be-Cu alloy with improved quasicrystalline forming ability
Zupanič, Franc ...
An Al94Mn2Be2Cu2 cast alloy was developed displaying increased quasicrystalline formation ability at moderate cooling rates. The as-cast microstructure consisted of a mainly icosahedral phase in the ...Al-matrix. The microstructure remained stable during uniform heating to 580 °C and isothermalannealing at 400 °C. Most of the icosahedral phase was preserved even after 24 h annealing at 500 °C. For that reason, this alloy presents a promising basis for further development of cast Al-alloys containing quasicrystals.
Bibliografsko gradivo je bilo uspešno dodano na polico.
Dodajanje bibliografskega gradiva na polico ni uspelo.
Gradivo je že na polici.
Trajna povezava
URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto
Faktor vpliva
Izdaja
Kategorija
Razvrstitev
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Izberite knjižnično izkaznico:
Baze podatkov,
v katerih je revija indeksirana
Ime baze podatkov
Področje
Leto
Povezave do osebnih bibliografij avtorjev
Povezave do podatkov o raziskovalcih v sistemu SICRIS
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Citiranje
Funkcionalnost trenutno ni na voljo. Prosimo, poskusite kasneje.
PDF