  • Tribological properties of poly-ether-ether-ketone (PEEK) produced at different processing temperatures [Elektronski vir]
    Zalaznik, Maša ...
    Poly-ether-ether-ketone is a high performance and temperature stable polymer whose incorporation into different applications is rapidly increasing. PEEK properties are contributed to its ... semi-crystalline structure that is developed during processing; therefore, the use of different processing temperatures could alter , we have produced PEEK samples with variation of compression moulding where compression was separated from a heating part. This enabled us to use different processing temperatures, even those under a melting point of PEEK (300-400 C). Produced samples were tested in a reciprocating sliding regime in a dry sliding contact and evaluated in terms of friction, wear, hardness and transfer film formation. The results show that processing temperature has a great influence on wear performance and hardness of a material. Hardness was increased by higher processing temperature but, on the other hand, wear resistance was better at lower processing temperatures. Temperature influence was also seen in transfer film formation and in the appearance of worn surfaces.
    Vir: Polytrib 2014 [Elektronski vir] : proceeding (Datoteka Posters/1_ZALAZNIK_Tribological properties of poly-ether-ether-ketone (PEEK) produced at different processing temperatures.pdf (5 f.))
    Vrsta gradiva - prispevek na konferenci
    Leto - 2014
    Jezik - angleški
    COBISS.SI-ID - 13691163

vir: Polytrib 2014 [Elektronski vir] : proceeding (Datoteka Posters/1_ZALAZNIK_Tribological properties of poly-ether-ether-ketone (PEEK) produced at different processing temperatures.pdf (5 f.))
loading ...
loading ...
loading ...

Vnos na polico