Critical failure analysis of superheater tubes of coal-based boilerGupta, Gagan Kumar ; Chattopadhyaya, SomnathThis paper highlights a methodology for failure investigation of superheater tubes made of the material T-22 of a coal-based boiler. The process includes visual observation, the identification of ... sampling locations, the determination of the bulk chemical composition of the base alloy, microstructural investigation using optical microscopy, the exploration of finer structural details using a scanning electron microscope (SEM), the evaluation of hardness over samples obtained from different locations, the fractographic analysis of different failed locations, the X-ray diffraction (XRD) study of corrosion products adhered to inner surfaces, and the determination of the nature of the failure. Within a span of four months, three successive failures of superheater tubes were reported. The tubes were observed to have undergone significant wall thinning. Microscopic examinations using SEM on the failed region and a region some distance away on the as-received tubes were conducted in order to determine the failure mechanism. Layer-wise oxidation corrosion (exfoliation) in the inner surface was observed. Apart from major cracking, a number of nearly straight line crackings were observed in the longitudinal direction of both tubes. Close to cracking/bulging, void formation/de-cohesion of grain boundary indicated creep deformation under service exploitation. The failure mechanism was identified to be a result of excessive oxidation corrosion along the inside wall to reduce thickness, the spheroidization of alloy carbides and the coarsening of precipitate as well as creep void formation along grain boundary leading to inter-granular cracking with material flow near regions covered with thick scales. Moreover, there was a drastic reduction in bulk hardness of alloy and finally "thin lip fish mouth" fractures.Vir: Strojniški vestnik = Journal of mechanical engineering. - ISSN 0039-2480 (Vol. 63, no. 5, May 2017, str. 287-299, SI 43)Vrsta gradiva - članek, sestavni delLeto - 2017Jezik - angleškiCOBISS.SI-ID - 15502107
Avtor
Gupta, Gagan Kumar |
Chattopadhyaya, Somnath
Teme
coal based boiler |
corrosion |
creep |
fractographic analysis |
SEM |
superheater tube |
kotel na premog |
korozija |
fraktografska analiza |
SEM |
cev pregrevalnika |
XRD |
lezenje
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: Strojniški vestnik = Journal of mechanical engineering. - ISSN 0039-2480 (Vol. 63, no. 5, May 2017, str. 287-299, SI 43)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Gupta, Gagan Kumar | ![]() |
Chattopadhyaya, Somnath | ![]() |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: