  • Synthesis and structural properties of titanium containing microporous/mesoporous silicate composite (Ti, Al)-Beta/MCM-48
    Mazaj, Matjaž ...
    Thermally stable titanium-containing microporousžmesoporous composite (Ti, Al)-BetažMCM-48 was synthesised hydrothermally in the presence of structure-directing agents cetyltrimethylammonium bromide ... (CTABr), polyoxyethylene(8) isooctylhexyl ether (Tritonr X-114) and tetraethylammonium hydroxide (TEAOH) in the absence of sodium cations. The presence of both microporous and mesoporous phases was determined by XRD and HRTEM measurementsand by the analysis of nitrogen adsorption isotherm based on the Ž-plot method. The mass percentage ( ) of the microporous material in the composite is approximately 6.5%. NMR investigations showed that acid sites related to framework aluminium were generated by calcination of the as-synthesised (Ti, Al)-BetažMCM-48. Local environment of titanium incorporated into the microporousžmesoporous silicate material was investigated by X-ray absorption spectroscopy. XANES studies showed the presence of tetrahedrally-coordinated Ti4+ cations in the template-free sample. EXAFS analysis revealed that titanium cations were coordinated to fouroxygens in the first coordination shell, to one oxygen at 1.73(1) A and three oxygens at 1.86(1) A. In the second coordination sphere three silicon atoms were found at distances 3.18(2) A and 3.48(2) A, respectively. These results indicated framework Ti and thus the presence of Ti oxidation centres within the composite material.
    Vrsta gradiva - prispevek na konferenci
    Leto - 2007
    Jezik - angleški
    COBISS.SI-ID - 3636250