  • Properties of particleboards made by using an adhesive with added liquefied wood = Lastnosti ivernih plošč, izdelanih z uporabo lepila z dodanim utekočinjenim lesom
    Čuk, Nataša, 1981- ; Kunaver, Matjaž ; Medved, Sergej
    In this study, three-layer particleboards were produced using liquefied wood in an adhesive mixture. The influence of two different formaldehyde resins: melamine-formaldehyde and ... melamine-urea-formaldehyde resin and two various catalysts: ammonium sulfate and ammonium formate on the particleboard properties was investigated. There were also two pressing parameters examined: temperature and time. The following physical and mechanical properties of particleboards were measured: board thickness, density, moisture content, bending strength and modulus of elasticity, internal bonding strength, surface soundness, thickness swelling and formaldehyde content. The results showed that properties of produced particle boards were better when melamine-formaldehyde resin and ammonium formate as a catalyst were used in combination with liquefied wood in the adhesive mixture. Also, mechanical properties were improved as the press time and press temperature increased. The optimal mechanical properties of particleboards made with the utilization of the liquefied wood in the adhesive mixture were achieved at 3 min press time and 180 °C press temperature using melamine-formaldehyde resin and 3 % of ammonium formate as a catalyst. A very important characteristic is the low formaldehyde content and that is extremely important in the provision of better quality of life. With the liquefaction of wood and the application of liquefied wood in the particleboard production wood biomass exploitation could be significantly increased. We are able to produce new materials from renewable resources that can be a great alternative to the raw materials, originating from crude oil.
    Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 45, št. 3, 2011, str. 241-245)
    Vrsta gradiva - članek, sestavni del
    Leto - 2011
    Jezik - angleški
    COBISS.SI-ID - 859818