  • Oxidation of the Al2O3-TiB2 composites produced with the reduction-combustion synthesis technique = Oksidacija kompozita Al2O3-TiB2, izdelanega s tehniko redukcijske zgorevne sinteze
    Ergin, Nuri ; Garip, Yigit ; Ozdemir, Ozkan
    In this study, Al2O3-TiB2 composites were synthesized in an electrical resistance furnace in open atmosphere under the uniaxial pressure of 150 MPa at 1200 °C for 4 h, using the reduction-combustion ... synthesis technique. The initial powder mixture used in this study is Al+TiO2+B2O3. TiB2, Al2O3 and some trace phases were found in the produced composites using the X-ray diffraction analysis. The densities of the samples were measured using the Archimedes' technique. The relative density was determined as 94.2 % for the composites. The oxidation properties of the composites were examined in open atmosphere at 600 °C, 800 °C and 1000 °C after up to 64 h. The activation energy of the composite was calculated to be 90 kJ/mol.
    Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 47, št. 5, sep.-okt. 2013, str. 669-671)
    Vrsta gradiva - članek, sestavni del ; neleposlovje za odrasle
    Leto - 2013
    Jezik - angleški
    COBISS.SI-ID - 1022122

    Povezava(-e):

    http://mit.imt.si/Revija/
    Digitalna knjižnica Slovenije - dLib.si

vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 47, št. 5, sep.-okt. 2013, str. 669-671)

loading ...
loading ...
loading ...

Vnos na polico