  • Characterisation of a new dental alloy with high Au content
    Rudolf, Rebeka ...
    The basis for developing a new dental alloy with high Au content is appropriate chemical composition and manufacturing technology. This new Au dental alloy is based on the ternary system of Au-Pt-Zn ... with a nominal composition of 88.5Au-8.7Pt-1.5Zn-0.5In-0.4Ir-0.3Rh. The alloy was melted and cast in a vacuum-induction melting furnace in Zlatarna Celje. Casting was followed with subsequent thermo-mechanical treatment (procedures of profile and polish milling, thermal treatment) and cutting-off strips to form a regular shape. The heat treatments of Au alloy samples were carried out in a tube furnace under different temperatures, and over different times. Testing of the new Au dental alloy included examining the initial cast, and the different heat treated conditions of the Au alloy. The optical properties of Au-dental alloy were investigated by means of spectrophotometric colourimetry. Finally the test of cytotoxicity of new Au based dental alloys using standard in vitro assays for testing the biocompatibility with establishing new, more sensitive, in vitro tests on cell lines was done.
    Vir: RMZ - Materials and geoenvironment : periodical for mining, metallurgy and geology = RMZ - Materiali in geookolje : revija za rudarstvo, metalurgijo in geologijo. - ISSN 1408-7073 (Letn. 54, št. 3, jul. 2007, str. 303-318)
    Vrsta gradiva - članek, sestavni del
    Leto - 2007
    Jezik - angleški
    COBISS.SI-ID - 12059926