Characterization of defects in PVD TiAlN hard coatings = Karakterizacija defektov PVD TiAlN trdih prevlekGselman, Peter ...PVD hard coatings are continuously gaining their importance in different fields of applications. In industrial use, they are often exposed to corrosive environments. Hard coatings possess inherently ... good corrosion resistance, but the substrate-hard coating systems may suffer from a severe corrosion attack due to the defects (craters, pin holes) in the coatings. On the sites, where defects extend through the coating, pitting corrosion can take place. These sites are drawbacks in the applications of hard coating. A PVD TiAlN hard coating was prepared on cold-work, tool-steel (AISI D2) substrates by sputtering using unbalanced magnetron sources. The growth defects incorporated into the coating were studied after the deposition and corrosion experiments. We used two methods: (1) scanning electron microscopy (SEM) for general overview of the coating topography and 2D-characterization of defects, and (2) scanning electron microscopy with a focused ion beam (SEM-FIB) for making serial cross-sections through the selected defects in order to provide images for a 3D-reconstruction of defects. In this work we tried to investigate the formation of a defect at a specific location and findout whether the selected defect causes pitting corrosion.Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 46, št. 4, jul.-avg. 2012, str. 351-354)Vrsta gradiva - članek, sestavni delLeto - 2012Jezik - angleškiCOBISS.SI-ID - 16153622
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 46, št. 4, jul.-avg. 2012, str. 351-354)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Gselman, Peter | 33428 |
Bončina, Tonica | 14334 |
Zupanič, Franc | 12295 |
Panjan, Peter, 1957- | 09090 |
Kek-Merl, Darja | 12616 |
Čekada, Miha | 18271 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema:
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi