Corrosion of Al/SiC metal-matrix composites = Korozija kompozitov Al/SiCTandler, Marko ...Discontinuously reinforced (DR) Al/SiC metal-matrix composites (MMCs) are modern, lightweight materials which have a very attractive combination of material properties and price. The use of DR Al/SiC ... MMCs is mostly limited to the military and aerospace, however, these materials are now beginning to penetrate civilian applications. Besides the mechanical behavior, a knowledge of the corrosion resistance of DR Al/SiC MMCs is very important, and so the corrosion resistance of Al/SiC composites has been investigated and discussed in comparison with a conventional Al alloy of similar composition. The results of the investigation show that the conventional unreinforced AlSi7Mg1 alloy has a better corrosion resistance in both the selected corrosion media. The best corrosion resistance is obtained in a 3.5 % water solution of NaCl: a corrosion medium that is comparable with aggressive sea water. Corrosion-resistance investigations showed that corrosion cracking did not occur as a result of stress corrosion. Only general surface corrosion was observed, which is reflected in a significant reduction in the area of the investigated samples. The reduction in area is a consequence of hydrogen embrittlement.Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 34, št. 6, nov.-dec. 2000, str. 353-358)Vrsta gradiva - članek, sestavni delLeto - 2000Jezik - angleškiCOBISS.SI-ID - 209247
Avtor
Tandler, Marko |
Šuštaršič, Borivoj |
Vehovar, Leopold |
Torkar, Matjaž
Teme
korozija |
kompoziti |
aluminij |
silicijev karbid |
karakterizacija
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 34, št. 6, nov.-dec. 2000, str. 353-358)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Tandler, Marko | 17081 |
Šuštaršič, Borivoj | 08195 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema:
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi