As-rolled multi-phase microalloyed steel bars with improved properties = Valjane večfazne mikrolegirane jeklene palice z izboljšanimi lastnostmiDrobnjak, Djordje ; Koprivica, A.ǂA ǂseries of experimental steels, based on a 0.3 C, 1.5 Mn, 0.1 V composition, with and without 0.01% Ti addition, was made by laboratory and full scale casting, and fabricated into 22 mmdia bars by ... full-scale hot-rolling. Multi phase Polygonal Ferrite-Pearlite-Non Polygonal Ferrite (PF-P-NPF) structures with varying amount of NPF are obtained in as-rolled bars. Acicular Ferrite (AF) and classical Bainite Sheaves (BS) are found to be dominant NPF morphologies in steels with a low (<30%) and a high (>40%) fraction of NPF, respectively. In Ti-bearing PF-P-AF steels, the PF-grain and P-colony size control, obtained through fine TiN particles, which also provide preferential sites for intragranular nucleation of AF, a tensile strength of 800/850 MPa and 900/950 MPa in 0.2 and 0.3 C steels was obtained, while maintaining the room temperature CVN impact energy at a level of 65/75 J and 40/50 J, respectively. A high fraction of grain boundary nucleated BS is promoted by increasing the content of Cr, Mo or Mn above the base level. The main effect of introducing BS into structure is a drop in impact toughness. Even so, in some BS dominated steels (notably Cr treated) an impact energy of 30/35 J is maintained at a tensile strength level of 1050/1100 MPa. These results have provided a bases for the development of as-rolled medium carbon mycroalloyed engineering bars, that achieve satisfactory properties in the as-rolled conditions without the need for subsequent heat treatment.Vir: Kovine zlitine tehnologije = Metals alloys technologies. - ISSN 1318-0010 (Letn. 31, št. 6, nov.-dec. 1997, str. 533-537)Vrsta gradiva - članek, sestavni delLeto - 1997Jezik - angleškiCOBISS.SI-ID - 71338
Avtor
Drobnjak, Djordje |
Koprivica, A.
Teme
jekla |
mikrolegirano jeklo |
faze |
struktura |
mikrolegiranje |
palice |
mehanske lastnosti
vir: Kovine zlitine tehnologije = Metals alloys technologies. - ISSN 1318-0010 (Letn. 31, št. 6, nov.-dec. 1997, str. 533-537)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema:
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi