Influence of the foaming precursor's composition and density on the foaming efficiency, microstructure development and mechanical properties of aluminium foams = Vpliv sestave in gostote prekurzorjev za penjenje na učinkovitost penjenja ter razvoj mikrostrukture in mehanskih lastnosti aluminijskih penKevorkijan, Varužan ...In this work, the influence of the composition, density and porosity of foaming precursors on the foaming efficiency, microstructure development and mechanical properties of aluminium foams are ... presented and discussed. The foams were prepared, starting from precursors made either by powder metallurgy (PM) or by the melt route. Following the PM route, precursors were made by mixing Al powder and 3-10 % of volume fractions of dolomite or calcium carbonate particles of particle size from 20 [mu]m to 120 [mu]m and cold isostatically pressing the mixture at 700 MPa. In the case of the melting route, precursors were made by introducing dolomite or calcium carbonate particles directly into the molten aluminium at 700 [compositum]C. After melt stirring, the precursors were prepared by casting the semi-solid slurry into a cylindrical, water-cooled mould. Finally, aluminium foams were made in all cases by inserting precursors into a cylindrical stainless-steel mould and heating the arrangement at 750 [compositum]C for 10 min. After that, the mould was removed from the furnace and the foaming process was stopped by cooling in air to room temperature. The microstructure of the obtained foams was investigated by optical and scanning electron microscopy (SEM-EDS), while XRD was applied for a detailed identification of phases. The quality of the precursors was evaluated by determining their mechanical properties (uniaxial room-temperature compression stress-strain curve, compressive strength and energy absorption after a 30 % strain) and the foaming efficiency (the relative density of the foam obtained). The concentration of the foaming agent and the density of precursors were found to have a detrimental influence on the foaming efficiency as well as on the foam's microstructure and mechanical properties. The foaming of precursors with open porosity were inefficient.Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 45, št. 2, mar.-apr. 2011, str. 95-103)Vrsta gradiva - članek, sestavni delLeto - 2011Jezik - angleškiCOBISS.SI-ID - 856490
vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 45, št. 2, mar.-apr. 2011, str. 95-103)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Kevorkijan, Varužan | 04968 |
Škapin, Srečo D. | 11093 |
Paulin, Irena | 28660 |
Šuštaršič, Borivoj | 08195 |
Jenko, Monika, metalurginja | 05675 |
Lažeta, Marjana | 15911 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema:
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi