Temperature behaviour of the boride layer of a low-carbon microalloyed steel = Temperaturno vedenje boridnega sloja na maloogljičnem mikrolegiranem jeklu
Ucar, Nazim ; Aytar, Omer Baris ; Calik, Adnan
In this work, the boronizing of low-carbon microalloyed steels was carried out in a solid medium using the powder-pack method. After boronizing, a boride layer and the presence of both FeB and Fe2B ...phases in the boride layer were revealed with classic metallographic techniques and X-ray diffraction (XRD) analysis. The presence and distribution of alloying elements on the boride phases was measured using glow-discharge optical emission spectrometry (GDOES) and the distance between the surface and the substrate was taken as the layer thickness. It was found that higher boronizing temperatures resulted in an increase in the layer thickness, from 7 [mu]m to 105 [mu]m. In addition, microhardness tests of the boronized steel samples showed a significant increase in the surface hardness caused by the increased boronizing temperature. The boride layer had a hardness of over 910 HV0.1 and 1320 HV0.1 for 973 K and 1273 K, respectively, while the substrate's hardness was approximately 145 HV0.1. Kinetic studies showed that the diffusion process is thermally activated, with the mean value of the activation energy being close to 194 kJ/mol.
Bibliografsko gradivo je bilo uspešno dodano na polico.
Dodajanje bibliografskega gradiva na polico ni uspelo.
Gradivo je že na polici.
Trajna povezava
URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto
Faktor vpliva
Izdaja
Kategorija
Razvrstitev
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Izberite knjižnično izkaznico:
Baze podatkov,
v katerih je revija indeksirana
Ime baze podatkov
Področje
Leto
Povezave do osebnih bibliografij avtorjev
Povezave do podatkov o raziskovalcih v sistemu SICRIS
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Citiranje
Funkcionalnost trenutno ni na voljo. Prosimo, poskusite kasneje.
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi