Characterization of an Cu-Cr-Zr alloy synthesized with the powder-metallurgy technique = Karakterizacija zlitine Cu-Cr-Zr, sintetizirane s tehniko prašne metalurgijeIpek, MedihaA Cu-1.5 % Cr-0.5 % Zr alloy was prepared with the powder-metallurgy (PM) method. Cu-Cr-Zr powders were pressed under 390 MPa of uniaxial compression and sintered at 1000 °C for 2 h. After the ... holding time, the samples were immediately taken out of the furnace and pressed at 850 MPa. The sintered samples were solution-treated at 1000 °C for 15 min and water quenched. Then they were deformed by 20 % at room temperature and aged at 470 °C for (2, 4, 6 and 8) h. A SEM investigation revealed that the Cr and Zr particles having a limited solubility in Cu distributed homogeneously in the copper matrix. An XRD analysis showed that each sample (sintered and aged at 470 °C for different times) has the same phases: copper and trace Cr[sub]{2}O[sub]3. The relative density of the sinter-pressed sample increased from 92 % to 96 % due to cold deformation. The microhardness of the samples ranged from 77 HV for the solution-treated and water-quenched sample to 116 HV for the aged sample, and the electrical conductivity of the samples increased from 76 % IACS for the sinter-pressed sample to 87 % IACS for the sample aged for 8 h.Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 47, št. 1, jan.-feb. 2013, str. 111-114)Vrsta gradiva - članek, sestavni delLeto - 2013Jezik - angleškiCOBISS.SI-ID - 961706
Avtor
Ipek, Mediha
Teme
bakrove zlitine |
prahovi |
prašna metalurgija |
sintranje |
utrjevanje s staranjem |
električna prevodnost |
trdota
vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 47, št. 1, jan.-feb. 2013, str. 111-114)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Ipek, Mediha |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema:
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi