S Arunkumar; Alphin M S; Z Edward Kennedy; N Sriraman
Materiali in tehnologije, 01/2022, Letnik: 56, Številka: 1Journal Article
This study enhances the strength of the Al6061 alloy by adding Ti in the form of a rod using a thermomechanical process, which would be useful in making structures for aerospace and structural members. Two different properties of the material are joined together to form a new bimetallic material. Softer Al-6061 is used as a sleeve, and grade-II Ti is used as a core. They were prepared with a co-extrusion process at a temperature of 400 °C with different ratios of 2:1 and 2:0.5. The prepared substrates are analysed for characterization, hardness, tensile strength, and corrosion. The development of the diffusion layer is observed at the boundary of the Al-Ti material, and the bonding is improved. Compared to an aluminium alloy and a 2:1 bimetal composite, the co-extruded Al-Ti with a ratio of 2:0.5 bimetal composite ratio shows a better microstructure, mechanical, and tribological properties. It is concluded that the co-extrusion of Ti and Al is an efficient way to devise new composites with mechanical properties of 14% and 19%, respectively.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.