Hirayama, Y.; Takagi, K.
Journal of alloys and compounds, 07/2019, Letnik: 792Journal Article
We successfully prepared nanosized Fe-Co alloy powder directly by a thermal plasma process, although a small amount of unprocessed Co was observed in the X-ray diffraction results. The mean particle size was ∼90 nm. The processed alloy particles were found to be single crystals, as confirmed by EBSD measurement. When an initial mixed powder having an Fe: Co ratio of 70 : 30 was used as the starting material, the mean and standard deviation of the Co concentration were 26.7 at% and 3.0 at%, respectively. The saturation magnetization values were in agreement with the bulk value, indicating that this small amount of oxygen dose not greatly affect the value of mass magnetization. This research realized the first full magnetization of a bare FeCo nanosized powder without any reduction treatment. •The FeCo alloy fine powder was prepared by thermal plasma process.•Processed FeCo nano particle was single crystal.•The concentration distribution of Fe and Co is quantitively evaluated.•The full magnetization for bare FeCo nanopowder was obtained.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.