Yu, Xiaopeng; Wang, Ning; Chu, Wei; Liu, Ming
Chemical engineering journal (Lausanne, Switzerland : 1996), 10/2012, Letnik: 209Journal Article
La-modified NiMgAl catalysts derived from hydrotalcites exhibited remarkably enhanced stability during the carbon dioxide reforming of methane because of their strong resistance to coke deposition. The reduced Ni0.5Mg2.5AlO4.5 (a) and Ni0.5Mg2.5Al0.9La0.1O4.5 (b) catalysts and the spent Ni0.5Mg2.5AlO4.5 (c) and Ni0.5Mg2.5Al0.9La0.1O4.5 (d) catalysts. Display omitted ► Ni catalysts showed a narrow Ni0 particle-size distribution between 5 and 11nm. ► Adding La increased the basicity and surface Ni content of the NiMgAl catalysts. ► Introducing La significantly improved the stability of the NiMgAl catalysts. ► La inhibited coking by forming La2O2CO3 and improving basicity and Ni0 dispersion. La-promoted NiMgAl mixed-oxide catalysts derived from hydrotalcite were synthesized by coprecipitation for the carbon dioxide reforming of methane. X-ray diffraction, thermogravimetric analysis, temperature-programmed reduction, X-ray photoelectron spectroscopy, temperature-programmed desorption of carbon dioxide, hydrogen chemisorption and transmission electron microscopy were used to investigate the structure and deactivation characteristics of the catalysts. The catalysts exhibited a narrow Ni-metal particle-size distribution between 5 and 11nm. The presence of lanthanum evidently improved reforming activity in the temperature range of 600–700°C, because the introduction of lanthanum into the NiMgAl catalysts increased the total amount of basic sites and the surface Ni content. The activity of the Ni0.5Mg2.5Al0.9La0.1O4.5 catalyst was slightly higher than those of the other lanthanum-containing catalysts. The addition of lanthanum improved the stability of the NiMgAl catalysts significantly because of the suppression of coke deposition. Lanthanum effectively inhibited coking by increasing the basicity of the catalysts, forming the La2O2CO3 phase and improving nickel metal dispersion.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.