Influence of substrate pre-treatment on the tribological properties of hard coatings during sliding
Podgornik, Bojan, 1970-
Hard PVD coating are usually very thin and brittle and so the substrate must carry the main part of the applied load. If the substrate has insufficient strength to carry the contact load and thus ...support the coating, plastic deformation will occur, leading to premature failure of the coating. In this thesis, the influence of the substrate pre-treatment on the tribological properties of hard PVD coatings was studied in terms of microhardness, residual stress, scratch adhesion and the dry sliding wear resistance. Surface treatment of the steel substrate involved hardening with two different tempering temperatures and plasma nitriding with or without a compound layer, while three PVD coatings were deposited on the pre-treated steel substrate: TiN, TiAlN and a hydrogen-free hard-carbon coating. Special emphasis was put on the influence of the hardness and residual stress distribution in the substrate as well as the interfacial bonding on the load carrying capacity and durability of the hard coating. Therefore, results of a number of wear tests in which flat-ended duplex-treated pins were mated to hardened ball bearing steel discs including various surface and subsurface analyses are presented in this thesis. In order to verify the suggested influence of the residual stress present in the pre-treated steel substrate, calculations of contact stress were carried out. The results of this investigation show improved wear properties of the plasma-nitrided hardcoated specimens compared with uncoated and pre-hardened ones. Increased hardness of the substrate, obtained by plasma nitriding, improves the load-carrying capacity of the substrate, which can then effectively support the coating, while interdiffusion between the iron-nitride at the nitrided surface and the thin Ti interlayer deposited at the beginning of the coating process most probably improves coating-to-substrate adhesion. Although previous investigation showed a negative effect of the compound layer, it was found that a precisely controlled plasma nitriding process can lead to a dense, uniform and highly adherent compound layer with a positive effect on the wear properties of pre-nitrided and hard-coated steel.
Type of material - scientific monograph
; adult, serious
Edition - Reprinted from the doctoral thesis
Publication and manufacture - Ljubljana : Center for Tribology and Technical Diagnostics, 2000
oddelek za odrasle 0000000053 PODGORNIK, Bojan Influence ... IN: 10120780
oddelek za odrasle 53 PODGORNIK, Bojan Influence ... IN: 10120780
available - outside loan, loan period: 1 months
Shelf entry
Adding material to shelf was successful.
Adding material to shelf failed.
It was not necessary to add the material to the shelf.
Bibliographic material was successfully added on shelf.
Adding bibliographical material on shelf was not successful.
Material is already on the shelf.
Permalink
URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year
Impact factor
Edition
Category
Classification
JCR
SNIP
JCR
SNIP
JCR
SNIP
JCR
SNIP
Select the library membership card:
DRS,
in which the journal is indexed
Database name
Field
Year
Links to authors' personal bibliographies
Links to information on researchers in the SICRIS system
Subject headings in COBISS General List of Subject Headings
Select pickup location
The material from the parent unit is free. If the material is delivered to the pickup location from another unit, the library may charge you for this service.