  • Hot rolling of the superaustenitic stainless steel AISI 904L = Vroče valjanje superavstenitnega nerjavnega jekla AISI 904L
    Tehovnik, Franc ...
    The AISI 904L superaustenitic stainless steel has a narrow processing window. In this work the hot rolling of steel, specifically the hot deformation behavior, is investigated. Specimens of steel ... were hot rolled at temperatures from 1000 °C to 1250 °C with 50 °C increments and the rolling loads were measured and recorded. Microstructural changes were examined, with the accent on the recrystallization. From changes of the hot-rolling loads and microstructure it is concluded that the recrystallization begins at temperatures around 1050 °C and three passes of 20 % deformation at the deformation rate of 5 s-1. In order to avoid over loads of rolling stand at equal deformation rate and degree, the recommended temperature was 1100 °C. The upper hot-working temperatures were not as clearly determined, it is considered to be around 1250 °C.
    Source: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 48, št. 1, jan.-feb. 2014, str. 137-140)
    Type of material - article, component part ; adult, serious
    Publish date - 2014
    Language - english
    COBISS.SI-ID - 1014698

    Link(s):

    http://mit.imt.si/Revija/
    Digitalna knjižnica Slovenije - dLib.si

source: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 48, št. 1, jan.-feb. 2014, str. 137-140)

loading ...
loading ...
loading ...

Shelf entry