Bennett, Chonlada; Sojithamporn, Phanumas; Thanakulwattana, Warinthorn; Wattanutchariya, Wassanai; Leksakul, Komgrit; Nakkiew, Wasawat; Jantanasakulwong, Kittisak; Rachtanapun, Pornchai; Suhr, Jonghwan; Sawangrat, Choncharoen
Materials, 12/2022, Volume: 15, Issue: 23Journal Article
This research was aimed at developing a dental prototype from 3D printing technology using a synthetic filament of polylactic acid (PLA) and zirconium dioxide (ZrO ) with glycerol and silane coupling agent as a binder. A face-centered central composite design was used to study the effects of the filament extrusion parameters and the 3D printing parameters. Tensile and compressive testing was conducted to determine the stress-strain relationship of the filaments. The yield strength, elongation percentage and Young's modulus were also calculated. Results showed the melting temperature of 193 °C, ZrO ratio of 17 wt.% and 25 rpm screw speed contributed to the highest ultimate tensile strength of the synthetic filament. A Nozzle temperature of 210 °C and an infill density of 100% had the most effect on the ultimate compressive strength whilst the printing speed had no significant effects. Differential scanning calorimetry (DSC) was used to study the thermal properties and percentage of crystallinity of PLA filaments. The addition of glycerol and a silane coupling agent increased the tensile strength and filament size. The ZrO particles induced the crystallization of the PLA matrix. A higher crystallization was also obtained from the annealing treatment resulting in the greater thermal resistance performance of the dental crown prototype.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.