Fan, K.L.; He, G.Q.; Liu, X.S.; Liu, B.; She, M.; Yuan, Y.L.; Yang, Y.; Lu, Q.
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 12/2013, Volume: 586Journal Article
The mechanical properties were evaluated on specimens of AlSi9Cu3–T6 (333-T6) gravity casting (GC) alloy at room temperature. The GC 333-T6 alloy showed higher yield strength (YS), ultimate tensile strength (UTS) and quality Index but lower hardening capacity than GC 333 aluminum alloy without heat treatment. In addition, the GC 333-T6 aluminum alloy offered a five-fold higher hardening capacity in the cyclic deformation than in the monotonic deformation. Cyclic deformation characteristics of GC 333-T6 aluminum alloy were obtained from the LCF test. The alloy exhibited cyclic stabilization at low strain amplitudes (0.2%) and cyclic hardening at higher strain amplitudes (0.25–0.35%). The extent of cyclic hardening increased with increasing strain amplitude. The Basquin' s equation and Coffin–Manson relationships could be used to describe the fatigue lifetime of this alloy. Additionally, micro-cracks initiated at pores would preferentially pass through the elongated Si particles at lower strain amplitudes. The fatigue crack propagation was mainly characterized by the formation of dimples or fatigue striations at different strain amplitudes. Meanwhile, the larger fatigue crack propagation zone and smaller spacing of fatigue striations at the lower total strain amplitude (0.2%) gave rise to a longer fatigue life. Furthermore, final fast fracture tended to preferentially occur from the larger defects in the fast-fracture region, such as large voids, small pits and inclusions.
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.