Ye, Beilin; Wen, Tongqi; Huang, Kehan; Wang, Cai‐Zhuang; Chu, Yanhui
Journal of the American Ceramic Society, July 2019, Volume: 102, Issue: 7Journal Article
The formation possibility of (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C high‐entropy ceramic (HHC‐1) was first analyzed by the first‐principles calculations, and then, it was successfully fabricated by hot‐pressing sintering technique at 2073 K under a pressure of 30 MPa. The first‐principles calculation results showed that the mixing enthalpy and mixing entropy of HHC‐1 were −0.869 ± 0.290 kJ/mol and 0.805R, respectively. The experimental results showed that the as‐prepared HHC‐1 not only had an interesting single rock‐salt crystal structure of metal carbides but also possessed high compositional uniformity from nanoscale to microscale. By taking advantage of these unique features, it exhibited extremely high nanohardness of 40.6 ± 0.6 GPa and elastic modulus in the range from 514 ± 10 to 522 ± 10 GPa and relatively high electrical resistivity of 91 ± 1.3 μΩ·cm, which could be due to the presence of solid solution effects.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.