Gao, Qi; Ye, Qing; Han, Shuai; Cheng, Shuiyuan; Kang, Tianfang; Dai, Hongxing
Catalysis Surveys from Asia, 06/2020, Volume: 24, Issue: 2Journal Article
The Ce-Cu-SAPO-18 samples were prepared by the ion exchange method. Physicochemical properties of the samples were systematically characterized by a number of analytical techniques, and Ce doping and hydrothermal temperature effects on NH.sub.3-SCR activity of Cu-SAPO-18 were also investigated. The results show that doping of Ce increased NH.sub.3-SCR activity and hydrothermal stability of the Cu-SAPO-18 sample. After Ce doping, a more amount of the isolated Cu.sup.2+ ions entered the D6R and the catalyst structure was more stable. The structure and catalytic activity of Ce-Cu-SAPO-18 remained almost intact after hydrothermal aging at 650 °C. After hydrothermal aging at 850 °C, however, the structure of Ce-Cu-SAPO-18 was greatly destroyed, and its catalytic activity declined remarkably. The high-temperature hydrothermal aging treatment led to decreases in amount of the isolated Cu.sup.2+ ions and acidic sites, destroying in the zeolitic structure, and drop in NH.sub.3-SCR activity.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.