  • Microstructure evolution in SAF 2507 super duplex stainless steel = Razvoj mikrostrukture v superdupleksnem nerjavnem jeklu SAF 2507
    Tehovnik, Franc ...
    The change of microstructure for a super duplex stainless steel SAF 2507 during hot rolling was investigated. Its evolution during hot deformation was very different in each phase. The dominant ... restoration mechanism for ferrite and austenite were dynamic recovery (DRV) and dynamic recrystallization (DRX), respectively. Also, the effect of temperature on the deleterious phase precipitation was investigated. The specimens were heat treated isothermally in the temperature range 800 [compositum]C to 1000 [compositum]C. Hardness tests, and optical and scanning electron microscopy were used to detect the sigma phase.
    Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 45, št. 4, jul.-avg. 2011, str. 339-345)
    Vrsta gradiva - članek, sestavni del
    Leto - 2011
    Jezik - angleški
    COBISS.SI-ID - 866474

    Povezava(-e):

    Digitalna knjižnica Slovenije - dLib.si

vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 45, št. 4, jul.-avg. 2011, str. 339-345)

loading ...
loading ...
loading ...

Vnos na polico