Application of powder metallurgy in the processing of aluminium scraps with high-iron contents = Uporaba postopkov prašne metalurgije za predelavo odpadkov na osnovi Al z visoko vsebnostjo FeVojtěch, Dalibor ; Průša, FilipThe Al-14Si-8Fe and Al-22Si-8Fe-1Cr (w/%) alloys were prepared via melt centrifugal atomization and compaction at a pressure of 6 GPa. The resulting alloys were porosity-free with good contacts ... between the particles. The structures were very fine and consisted of primary [alpha](Al) dendrites, eutectic silicon and the [betha]-Al5FeSi phase. The Vickers hardness values of the Al-14Si-8Fe and Al-22Si-8Fe-1Cr alloys were (170 10) HV5, (185 16) HV5, respectively. Compressive strength values were 670 MPa and 720 MPa, respectively. Surprisingly, both alloys exhibited a very good plasticity due to the refined structure. The alloys were annealed at 300-400 °C for 100 h to reveal their thermal stability. When the thermal stability of the powder-metallurgy Al-14Si-8Fe and Al-22Si-8Fe-1Cr alloys was compared to that of the casting-piston Al-12Si-1Cu-1Mg-1Ni alloy, the former was found to be superior.Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 46, št. 4, jul.-avg. 2012, str. 339-343)Vrsta gradiva - članek, sestavni delLeto - 2012Jezik - angleškiCOBISS.SI-ID - 936618
Avtor
Vojtěch, Dalibor |
Průša, Filip
Teme
aluminium |
powder metallurgy |
solidification |
iron |
aluminij |
metalurgija prahov |
strjevanje |
železo
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 46, št. 4, jul.-avg. 2012, str. 339-343)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Vojtěch, Dalibor | ![]() |
Průša, Filip | ![]() |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema:
Naročanje gradiva za izposojo v čitalnice
Naročanje kopij člankov
Urnik dostave gradiva z oznako DS v signaturi