This paper describes the development of poly(D,L-lactide-co-glycolide) (PLGA) nanoparticles (NPs) and nanosuspensions with the polyene antibiotic amphotericin B (AmB). The nanoformulations were ...prepared using nanoprecipitation and were characterised with respect to size, zeta potential, morphology, drug crystallinity and content. Standard in vitro sensitivity tests were performed on MRC-5 cells, red blood cells, Leishmania infantum promastigotes and intracellular amastigotes and the fungal species Candida albicans, Aspergillus fumigatus and Trichophyton rubrum. The in vivo efficacy was assessed and compared to that of Fungizone and AmBisome in the acute A. fumigatus mouse model at a dose of 2.5 and 5.0mg/kg AmB equivalents. The developed AmB nanoformulations were equivalently or more effective against the different Leishmania stages and axenic fungi in comparison with the free drug. The in vitro biological activity, and especially hemolytic activity, clearly depended on the preparation parameters of the different nanoformulations. Further, we demonstrated that the superior in vitro antifungal activity could be extrapolated to the in vivo situation. At equivalent dose, the optimal AmB-loaded PLGA NP was about two times and the AmB nanosuspension about four times more efficacious in reducing the total burden than AmBisome. The developed AmB nanomedicines could represent potent and cost-effective alternatives to Fungizone and AmBisome.
At 5.0mg/kg, the developed AmB-loaded PLGA NP was about two times and the AmB nanosuspension four times more efficacious in reducing the in vivo Aspergillus fumigatus burden than AmBisome. Display omitted
Colloidal carriers are known to improve the therapeutic index of the conventional drugs in the treatment of visceral leishmaniasis (VL) by decreasing their toxicity whilst maintaining or increasing ...therapeutic efficacy. This paper describes the development of poly(
d,
l-lactide-co-glycolide) (PLGA) nanoparticles (NPs) for the antileishmanial saponin β-aescin. NPs were prepared by the W/O/W emulsification solvent evaporation technique and the influence of five preparation parameters on the NPs’ size (
Z
ave), zeta potential and entrapment efficiency (EE%) was investigated using a 2
5−2 fractional factorial design. Cytotoxicity of aescin, aescin-loaded and blank PLGA NPs was evaluated in J774 macrophages and non-phagocytic MRC-5 cells, whereas antileishmanial activity was determined in the
Leishmania infantum ex vivo model. The developed PLGA NPs were monodispersed with
Z
ave
<
500
nm and exhibited negative zeta potentials. The process variables ‘surfactant primary emulsion’, ‘concentration aescin’ and ‘solvent evaporation rate’ had a positive effect on EE%. Addition of Tween
® 80 to the inner aqueous phase rendered the primary emulsion more stable, which in its turn led to better saponin entrapment. The selectivity index (SI) towards the supporting host macrophages increased from 4 to 18 by treating the cells with aescin-loaded NPs instead of free β-aescin. In conclusion, the
in vitro results confirmed our hypothesis.
Cyclosporine A loaded poly(lactide-co-glycolide) nanoparticles were prepared using the o/w emulsification solvent evaporation method and the effect of four preparation parameters on particle size and ...zeta potential was investigated. Release properties of the nanoparticles were examined
and in vitro experiments were performed in order to evaluate the cytotoxicity and anti-inflammatory activity of the nanoparticles developed. Particle sizes varied between 191 and 303 nm depending on the different preparation parameters and all nanoparticle dispersions were monodisperse.
The nanoparticles showed negative zeta potential values varying between −16 and −35 mV and 57 to 70 % of the amount of loaded cyclosporine A was released after 24 h. None of the nanoparticle formulations showed significant cytotoxicity compared to the negative control using human
epithelial cells (HaCaT). Cyclosporine A incorporated in the various nanoparticle formulations retained its anti-inflammatory activity as significant suppression of interleukine-2 secretion in concanavalin A stimulated Jurkat T cells was measured. As the overall influence of the freeze-drying
process on the characteristics of nanoparticles was limited, trehalose and carnitine should be preferred as cryoprotectants in ocular formulations for treatment of dry eye disease.
Drug delivery systems present an opportunity to potentiate the therapeutic effect of antileishmanial drugs. Colloidal carriers are rapidly cleared by the phagocytic cells of the reticuloendothelial ...system (RES), rendering them ideal vehicles for passive targeting of antileishmanials. This paper describes the development of poly(D,L-lactide-co-glycolide) (PLGA) nanoparticles (NPs) for the antileishmanial saponin β-aescin. NPs were prepared using the combined emulsification solvent evaporation/salting-out technique. Confocal microscopy was used to visualise the internalisation and intracellular trafficking of fluorescein- and nile red-labelled PLGA NPs in J774A.1 macrophages infected with GFP-transfected Leishmania donovani. The in vitro activity of aescin and aescin-loaded NPs on L. infantum was determined in the axenic model as well as in the ex vivo model. The developed PLGA NPs were monodispersed with Zave<300 nm, exhibited negative zeta potentials and had relatively high drug loadings ranging from 5.80 to 8.68% w/w PLGA. The fluorescent NPs were internalised by the macrophages and trafficked towards the lysosomes after 2 h in vitro incubation. Co-localisation of the NPs and the parasite was not shown. A two-fold increase in activity was observed in the ex vivo macrophage model by encapsulating β-aescin in PLGA NPs (IC50, 0.48-0.76 µg/mL vs. 1.55 ± 0.32 µg/mL for the free drug).
The objective of this study was to enhance the encapsulation of the antileishmanial saponin aescin in poly(D,L-lactide-co-glycolide) (PLGA) nanoparticles (NPs). We prepared the NPs by the O/W and ...W/O/W combined emulsification solvent evaporation/salting-out technique and investigated the influence of organic phase composition on the NPs' size, zeta potential and entrapment efficiency (EE%) using mixture designs. The obtained NPs were monodispersed with Z
ave
<300 nm and exhibited negative zeta potentials. For the single emulsion, the co-solvent concentration was shown to be the primary determinant of drug entrapment. The EE% increased from 14% to 22% by decreasing the amount of DMSO from 80% to 25% (v/v) in the organic polymer solution. For the double emulsion, EE% was 22% on average and independent of the organic phase composition. The double-emulsion technique did not enhance the aescin encapsulation as expected due to its amphiphilic nature. The optimised aescin-loaded NPs meet the requirements for further in vitro activity tests.
Objective: Ocular bioadhesive minitablets containing gentamicin and vancomycin were developed using different powder mixtures of pregelatinized starch and Carbopol (physical or cospray-dried ...mixtures). Methods: Drug content, antimicrobial activity, and radical formation of the powders used for tablet preparation were evaluated immediately and 30 days after gamma sterilization. Tablet properties and in vitro drug release from the sterilized minitablets were determined. Storage stability of vancomycin and gentamicin in sterilized bioadhesive mixtures was examined by LC-UV MS and a microbiological assay, respectively. A bioadhesive powder mixture containing only vancomycin was irradiated by X electron-magnetic radiation to evaluate vancomycin stability following sterilization through irradiation. Results: The antimicrobial activity of gentamicin against Staphylococcus epidermidis was not altered in comparison to nonsterilized formulations. Only after an overkill dose of 50 kGy, the concentration of vancomycin decreases to an extent that was pharmaceutically significant. No significant difference in radiation stability between drug substance and product (i.e., powder mixture) was observed. A shift in stability profile was not observed at 6 weeks after irradiation. All other degradation products were present only in small quantities not exceeding 1.0%. The in vitro drug release from the minitablets prepared with physical powder mixtures of pregelatinized starch and Carbopol® 974P NF (96 : 4) was faster compared to the cospray-dried mixtures of starch with Carbopol® 974P NF (ratio: 95:5 and 85:15). The electron paramagnetic resonance signals of the radicals formed during sterilization were still visible after storage for 30 days. The slug mucosal irritation test indicated mild irritation properties of the bioadhesive powder mixtures although no tissue damage was observed.
The purpose of this study was to evaluate different bioadhesive ocular formulations based on drum dried waxy maize
® starch (DDWM), Amioca
® starch and Carbopol
® 974P. The concentrations of Carbopol
...® 974P in the mixtures varied between 5 and 25% (w/w). The rheological properties of the non-sterilized and gamma-irradiated physical blends of Carbopol
® 974P with either DDWM or Amioca
® were compared to those of the corresponding co-spray dried Amioca
® starch/Carbopol
® powders. Higher viscosity or consistency values were measured for sterilized co-spray dried powder mixtures containing an amount of Carbopol
® 974P equal or above 15% (w/w) compared to the physical blends.
Sustained release minitablets (Ø 2
mm, 6
mg), consisting of sodium fluorescein as model drug and the bioadhesive powders, were manufactured at a compression force of 1.25
kN. Afterwards, the tablets were sterilized with gamma-irradiation. The amount of Carbopol
® in the co-spray dried powder mixtures on the one hand and gamma-irradiation on the other hand had no significant influence on the crushing strength and friability of the minitablets evaluated. However, these two factors affected the in vitro release properties of the minitablets. The slowest release was obtained with tablets containing 25% Carbopol
® 974P, which unfortunately possess mucosal irritating properties. By using co-spray dried Amioca
® with 15% (w/w) Carbopol
® 974P, a slower release can be achieved compared to the physical mixtures of DDWM or Amioca
® starch with Carbopol
® 974P. Moreover, this ocular formulation is very promising and is preferred, as it did not cause any mucosal irritation and released the model drug for at least 12
h, after application in the fornix.
The influence of the compression force on the physical properties, the in vitro release and the in vivo behavior of ocular minitablets is evaluated in the present study. The bioerodible minitablets ...(Ø 2 mm, 6 mg) were produced at different compression forces. The crushing strength, friability, water uptake, hydration and swelling of the minitablets both in vitro as well as in vivo after application in the cul-de-sac were evaluated. The friability remained below 1% only for the minitablets made at 0.500 and 0.750 kN. The crushing strength measured was 3.53±0.98, 12.34±1.69 and 18.64±2.37 N for minitablets made at 0.250, 0.500 and 0.750 kN, respectively. The full hydration time equalled 20 and 30 min for minitablets compressed at 0.250 kN and 0.500–0.750 kN, respectively. Increasing the compression force resulted in a decreased swelling capacity. The in vivo release was evaluated in healthy volunteers using a non-invasive method to measure the apparent sodium fluorescein concentration in the tearfilm–cornea compartment as a function of time. The longest residence time of the fluorescent tracer at the administration site was obtained by the minitablets compressed at 0.750 kN. The in vitro release was evaluated with three different dissolution methods: the reciprocating cylinder method, vials in an oscillatory shaking bath and a static method with vials. The best correlation with the in vivo behavior of the matrix minitablets was obtained with the shaking bath method.