  • The influence of copper on the decarburization and recrystallization of Fe-Si-Al alloys = Vpliv bakra na razogljičenje in rekristaizacijo zlitin Fe-Si-Al
    Steiner Petrovič, Darja ; Jenko, Monika, metalurginja ; Doleček, Valter
    The decarburization and recrystallization of Fe-Si-Al alloys containing copper was investigated. The decarburization annealing of non-oriented electrical steel sheets produced from Fe-Si-Al alloys ... depends on the chemical reactions between the gas mixture and the carbon at the steel's surface. The carbon diffusion, the temperature of decarburization annealing, the composition of the gas mixture and the chemical composition of the steel are the influencing parameters that determine the kinetics and the mechanism of decarburization. The decarburization of Fe-Si-Al alloy with the mass fraction of 0.24% and 0.43% of copper was compared with the decarburization of an Fe-Si-Al alloy with a very small amount of copper (0.01%). The decarburization annealing was performed in a H2-H2O gas mixture at 840 °C. The residual carbon content was determined by analytical chemical method. The alloys were also recrystallized in hydrogen at 980 °C. Microstructure of samples after decarburization and recrystallization annealing was investigated with optical microscopy.
    Vir: Materiali in tehnologije = Materials and technology. - ISSN 1580-2949 (Letn. 40, št. 1, 2006, str. 13-16)
    Vrsta gradiva - članek, sestavni del
    Leto - 2006
    Jezik - slovenski, angleški
    COBISS.SI-ID - 10297110

    Povezava(-e):

    Digitalna knjižnica Univerze v Mariboru – DKUM
    Digitalna knjižnica Slovenije - dLib.si

Vnos na polico