Mehanske in korozijske lastnosti lotanih in lasersko varjenih spojev stelitne zlitine : [magistrska naloga]Zupančič, RokBackground: The longevity of prosthetic restorations is often limited due to the mechanical or corrosive failure in places where parts of metal framework were joined. The conventional joining method ... is soldering, though recently laser welding became an available and far more practical alternative. Researchshows that for most dental alloys laser welded joints have greater tensile strength than soldered ones, demonstrating at the same time lower resistance to cyclic fatigue. The composition of the alloy significantly affects the quality of the laser welded joint. Corrosion resistance of soldered and laser welded joints has so far been compared by microscopical assessment of corrosion defects only. The quantitative comparison of electrochemical properties of different joints is not to be found in the literature. ObjectiveČ To determine which joining method offers the best mechanical and corrosion properties to Remanium GM 380 alloy frameworks we compared the properties of soldered joints with two types of laser welded joints. Materials and methodsČ For tensile testing cylindrical samples of Remanium GM 380 were cast. They were sectioned in the middle, perpendicular totheir long axis, and subsequently joined again using different methods. We formed three test groupsČ - soldering with a Co-Cr solder, - laser welding with a tight joint, - laser welding with the joint in the shape of the letter X. Tensile strength was measured using a Zwick Z 030 testing machine. For the assessment of corrosion properties, we formed the three forementioned test groups, and a controll group of intact cylindrical rods. We used electrochemical impedance spectroscopy and electrochemical potentiodynamic polarization. After mechanical and electrochemical testing, the fracture surfaces and corrosion defects were analized with a scanning electron rnicroscope. Longitudinal sections were analyzed on a metalographic optical microscope.Vrsta gradiva - magistrsko deloZaložništvo in izdelava - [Ljubljana] : [R. Zupančič], 2005Jezik - slovenskiCOBISS.SI-ID - 2806548
Avtor
Zupančič, Rok
Drugi avtorji
Funduk, Nenad |
Legat, Andraž
Teme
Dental alloys |
Dental soldering |
Methods |
Welding |
Methods |
Lasers |
Instrumentation |
Tensile strength |
Corrosion |
Dentalne zlitine |
Dentalno spajkanje |
Metode |
Varjenje |
Metode |
Laserji |
Inštrumentacija |
Natezna trdnost |
Korozija |
zobozdravstvo
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Knjižnica | Signatura – lokacija, inventarna št. ... | Status izvoda |
---|---|---|
MF, Centralna medicinska knjižnica, Ljubljana | magistrske naloge ZUPANČIČ Rok Mehanske IN: 020050601 |
prosto - na dom, čas izposoje: 1 mes. |
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Zupančič, Rok | 23504 |
Funduk, Nenad | 03369 |
Legat, Andraž | 08281 |
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Obvestilo
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Mesto prevzema | Status gradiva | Rezervacija |
---|
Prosimo, počakajte trenutek.