High coercivities in HDDR processed Sm-Fe-Ta-N magnets = Visoke koercitivnosti Sm-Fe-Ta-N magnetov dobljenih po HDDR postopkuŽužek Rožman, Kristina ; McGuiness, Paul J. ; Kobe, SpomenkaAn alloy of composition ▫$Sm_{13,8}Fe_{82,2}Ta_{4,0}$▫ was compared with a conventional ▫$Sm_{13,7}Fe_{86,3}$▫ material in order to assess its potential as a permanent magnet mataerial. The optimum ... conditions necessary to provide the highest coercivities using the HDDR process and for the HDDR process combined with milling were investigated. The coercitivities obtained after using the HDDR process and subsequent nitriding were 676,6 kA/m for the ▫$Sm_{13,8}Fe_{82,2}Ta_{4,0}N_x$▫ and 358,2 kA/m for the ▫$Sm_{13,8}Fe_{86,3}N_x$▫ samples. Coercivities of 1003,0 kA/m for ▫$Sm_{13,8}Fe_{86,3}N_x$▫ and 1273,6 kA/m ▫$Sm_{13,8}Fe_{82,2Ta_{4,0}N_x$▫ were achieved by reducing the paraticle size with milling prior to the HDDR process. Magnetic results were comparedwith the phase composition, determined using scanning electron microscopy (SEM) and X-ray diffraction (XRD). The better coercivities obtained with the Ta containing sample were found to be due to the presence of a much smaller amount of ▫$\alpha$▫Fe, a soft magnetic phase, with the ▫$TaFe_2$▫ phase forming in its place. The milling prior to the HDDR treatment improves the magnetic properties because of the small particle size which prevents the grains growing too laarge, with their consequent very negative effect on the coercivity.Vir: Kovine zlitine tehnologije = Metals alloys technologies. - ISSN 1318-0010 (Letn. 32, št. 6, 1998, str. 515-518)Vrsta gradiva - članek, sestavni del ; neleposlovje za odrasleLeto - 1998Jezik - angleškiCOBISS.SI-ID - 93098
Avtor
Žužek Rožman, Kristina |
McGuiness, Paul J. |
Kobe, Spomenka
Teme
HDDR |
SmFeN |
Ta |
koercitivnost |
mletje |
HDDR |
SmFeN |
Ta |
coercitivity |
milling
![loading ... loading ...](themes/default/img/ajax-loading.gif)
vir: Kovine zlitine tehnologije = Metals alloys technologies. - ISSN 1318-0010 (Letn. 32, št. 6, 1998, str. 515-518)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|---|
Žužek Rožman, Kristina | 18824 |
McGuiness, Paul J. | 18594 |
Kobe, Spomenka | 04355 |
Vir: Osebne bibliografije
in: SICRIS
Izberite prevzemno mesto:
Prevzem gradiva po pošti
Naslov za dostavo:
Med podatki člana manjka naslov.
Storitev za pridobivanje naslova trenutno ni dostopna, prosimo, poskusite še enkrat.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrano prevzemno mesto in naslov za dostavo ter dokončali postopek rezervacije.
S klikom na gumb "V redu" boste potrdili zgoraj izbrani naslov za dostavo in dokončali postopek rezervacije.
Obvestilo
Trenutno je storitev za avtomatsko prijavo in rezervacijo nedostopna. Gradivo lahko rezervirate sami na portalu Biblos ali ponovno poskusite tukaj kasneje.
Gesla v Splošnem geslovniku COBISS
Izbira mesta prevzema
Gradivo iz matične enote je brezplačno. Če je gradivo na mesto prevzema dostavljeno iz drugih enot, lahko knjižnica to storitev zaračuna.
Mesto prevzema | Status gradiva | Rezervacija |
---|
Rezervacija v teku
Prosimo, počakajte trenutek.
Rezervacija je uspela.
Rezervacija ni uspela.
Rezervacija...
Članska izkaznica:
Mesto prevzema: