Voronenkov, V V; Bochkareva, N I; Gorbunov, R I; Latyshev, P E; Lelikov, Y S; Rebane, Y T; Tsyuk, A I; Zubrilov, A S; Popp, U W; Strafela, M; Strunk, H P; Shreter, Y G
arXiv.org, 02/2019Paper, Journal Article
GaN films with thickness up to 3 mm were grown by halide vapour phase epitaxy method. Two growth modes were observed: the high temperature (HT) mode and the low temperature (LT) mode. Films grown in HT mode had smooth surface, however the growth stress was high and caused cracking. Films grown in LT mode had rough surface with high density of V-defects (pits), however such films were crack-free. The influence of growth parameters on the pit shape and evolution was investigated. Origins of pits formation and process of pit overgrowth are discussed. Crack-free films with smooth surface and reduced density of pits were grown using combination of the LT and HT growth modes.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.