Win Khun, Nay; Liu, Erjia; Senthilkumar, D.; Albert, Bensely; Mohan Lal, D. Mohan Lal
Tribology in industry, 6/2024, Letnik: 46, Številka: 2Journal Article
As-received (AsRec) EN24 steel was treated with conventional heat treatment (ConHeatTreat) without tempering followed by deep cryogenic treatment (DeepCryoTreat) as a supplemental treatment to study its tribological behaviour against alumina without or with mineral oil (MO) under different normal loads of 1 N and 5 N. The ConHeatTreat of the AsRec-EN24 obtained an 218.5% improvement in its hardness as the supplemental DeepCryoTreat of the ConHeatTreat-EN24 resulted in a 11.7% further improvement in its hardness. As a result, the ConHeatTreat-EN24 had the 67.5% and 56.3% lower wear volumes for 1 N and 5 N under dry condition and the 53.6% lower wear volume for 5 N under MO lubrication condition compared to those of the AsRec-EN24, respectively. The DeepCryoTreat-EN24 had the 11.5% and 39.7% lower wear volumes for 1 N and 5 N under dry condition and the unmeasurable wear volume for 5 N under MO lubrication condition compared to those of the ConHeatTreat-EN24, respectively. It could be concluded that the supplemental DeepCryoTreat further improved the hardness and thereby the abrasive wear resistance of the ConHeatTreat-EN24 under both dry and lubrication conditions.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.